阀门材质对照表
中国阀门、日本阀门、德国阀门、英国阀门、美国阀门及阀门标准规定的常用金属材料对照表
分 | 序 | 中国 | 日本 | 标准 | 美国 | 英国 | 德国 |
GB1220 | JIS | ISO683/13 | ANSI | Bs970 | DIN17440 | ||
铸 | 1 | WCA | G5151 SCPH1 |
| A216 WCA | 161Cr-430F | GS-C25 |
2 | ZG230-450 WCB | G5151 SCPH2 SC410 |
| A216 WCB |
|
| |
3 | WCC |
|
| A216 WCC |
|
| |
4 | ZG20CrMo |
|
| A217 Wc5 | 3100 B2 |
| |
5 |
| G5151 SCPH21 |
| A217 Wc4 | 1504 621E |
| |
6 | ZG15CrMoV |
|
|
| 3100 B3 |
| |
铸 | 7 | ZG00Cr18Ni10 | G5121 SCS19A |
| A351 CF3 | 1504 304C12E |
|
8 | ZGOCr18Ni9Ti | G5121 SCS13A |
| A351 CF8 | 1504 304C15E | G-X6CrNiMo1810 | |
9 | CF3M | G5121 SCS16A |
| A351 CF3M | 1504 316C12E |
| |
10 | ZGOCr18Ni12Mo2Ti | G5121 SCS14A |
| A351 CF8M | 1504 316C16E |
| |
11 | CF8M | G5121 SCS14A |
| A744 CF-8M | 3100 316C16 |
| |
12 | CF8C | G5121 SCS21 |
| A351 CF8C | 1504 347C17E | G-X7CrNiNb1189 | |
13 | CF8 | G5121 SCS13A |
| A744 CF-8 | 3100 304C15 | G-X6CrNi189 | |
14 | CF3 | G5121 SCS19A |
| A744 CF-3 | 3100 304C12 |
| |
锻 | 15 | ZGOCr17Ni4Cu4Nb | G5121 SCS24 |
| 17-4PH |
|
|
16 | 1Cr18Ni9 | SUS302 | 12 | 302,S30200 | 302S25 | X12CrNi188 | |
17 | 0Cr18Ni9 | SUS304 | 11 | 304,S3400 | 304S15 | X5CrNi189 | |
18 | 00Cr18Ni10 | SUS304L | 10 | 304L,S30403 | 304S12 | X2CrNi189 | |
19 | 0Cr25Ni20 | SUS310S |
| 310S,S31008 |
|
| |
20 | 0Cr17Ni12Mo2 | SUS316 | 20,20 | 316,S31600 | 316S16 | X5CrNiMo1810 | |
21 | 1Cr18Ni12Mo2Ti |
|
|
| 320S17 | X10CrNiMoTi1810 | |
22 | 0Cr18Ni12Mo2Ti |
|
|
| 320S17 | X10CrNiMoTi1810 | |
23 | 00Cr17Ni14Mo2 | SUS316L | 19,19 | 316L,S31603 | 320S12 | X2CrNiMo1810 | |
24 | 0Cr17Ni12Mo2N | SUS316N |
| 316N,S31651 |
|
| |
25 | 0Cr17Ni4Cu4Nb |
|
| 17-4PH |
| X2CrNiMoN1812 | |
26 | 0Cr17Ni13Mo2N | SUS316LN |
|
|
|
| |
27 | 0Cr18Ni12Mo2Cu2 | SUS316J1 |
|
|
| X10CrNiTi189 | |
28 | 1Cr18Ni9Ti |
|
|
|
| X10CrNiTi189 | |
29 | 0Cr18Ni10Ti | SUS321 | 15 | 321,S32100 | 321S21，321S20 |
| |
30 | 1Cr13 | SUS410 | 3 | 410,S41000 | 410S21 | X10Cr13 | |
31 | 0Cr13 | SUS410S | 1 | 410S | 403S17 | X7Cr13 | |
32 | 2Cr13 | SUS420J1 | 4 | 420S,S42000 | 420S37 | X20Cr13 | |
33 | 3Cr13 | SUS420J2 | 5 | 420S45 |
|
| |
34 | 4Cr13 | SUS420J2 | 5 | 431,S43100 | 431S29 | X22CrNi17 | |
35 | 0Cr17Ni14Cu4Nb | SUS630B |
| 630,S17400 |
| X7CrNiA1177 | |
36 | 00Cr25Ni20Mn3Mo3N |
|
|
| U3 |
| |
37 | 0Cr17Mn14Mo2N |
|
| A4 |
|
| |
38 | 00Cr20Ni25Mo4Cu2 |
| 904L |
| UB6 |
| |
39 | 00Cr15Ni60M16W4 |
|
| （哈氏C） |
|
| |
40 | 0Cr20Ni30Mo2Cu3 |
| (20号合金) |
|
|
| |
41 | 0Ni70Cu30Mn |
| （蒙耐尔） |
|
|
|
阀体材料：WCB碳钢。WCB相当于25或35碳钢，我在某些不知道是不是正确的资料上说是：W代表焊接， C代表铸造，zui后一个字母代表阀体钢的型号。如果照一楼如此说的话，应该是属于特殊材料的代号。
铸造时可以使用WCA、WCB、WCC等代号，分别代表ZG205-415、ZG250-485、ZG275-485