SUTE纬绑扎带
详细说明:环氧树脂浸渍玻璃纤维网状无纬绑扎带(符合沪Q/JBQR18-2001)
Epoxy Resin Treated Fiberglass Web Unindirectional Banding Tape (In According With Shanghai Q/JBQR18-2001) 具有网状结构的电工用网状无纬带是电机和变压器行业理想的紧固绑扎材料,不仅具有优良的柔软性和粘性,储存期达一年(5℃),而且拉开呈网状结构(拉开宽度为原带宽2倍以上),不散丝,无叠痕,退卷容易等特点。其优良性能还在于具有高抗张,高抗冲击,高模量、低延伸、无磁滞和无涡流等特点。
本产品不仅适用于普通电机转子、变压器芯子的紧固绑扎,还可以用于大型特种电机的绑扎,zui大绑扎力可达100N/mm。
Epoxy Resin Treated Fiberglass Banding Tape With Web Structure is an ideal banding material for applying to the electrical machines.This banding tape is not only pliable and slightly tacky but also can be unwinded freely from the spool with out glass strands separation and overlapping.When it is pulled open the web structure will appear and the width of the tape may be extended to over twice the swize of the original.It also can be storaged for one year at the temperature of 5℃.In addition,this product possesses its desitinctive characteristics of high tensile strength,high resistance to shock,high modulus of elasticity and low percent elongation at break as well as no magnetically-confining and eddy losses.
Banding armatures of rotating electrical machines or blocking transformer colums is not the only use of this tape,and also applicable to the large-scale and special type electrical machines ect.Its max pull,When banding,can reach 100N/mm.
型号Type | 环氧型Epoxyglass |
厚度Thickness(mm) | 0.30±0.03;0.20±0.02;0.17±0.02 |
宽度Width(mm) | 10±0.5;15±0.5;20±1.0;25±1.0 |
长度Length(mm) | 150±10;200±10 |
其它规格可协商Other type required can be supplied through negotiation.
主要技术性能Characteristics: |
挥发份 | Volatile content by weight | <5% | |||||
含胶量 | Resin content | 27±2% | |||||
可溶性树脂含量 | Solubility resin content | ≥90% | |||||
抗拉强度 | Teneile strength | 常态 Room temperture | ≥900MPa | ||||
热态 at 150℃ | ≥560MPa | ||||||
绝缘等级 | Thermal Class |
| F | ||||
储存期 | Storage life | 储存温度 Storage temperture℃ | 5 | 10 | 15 | 20 | 25 |
储存时间(月)Storage time | 12 | 8 | 6 | 4 | 3 | ||
固化条件 | Curing conditions | 温度 temperture℃ | 155 | ||||
时间(小时)Time(hours) | 6~10 | ||||||
产品使用率 | Utilization ratio |