FLTM_BI103标准盐雾试验箱

FLTM_BI103标准盐雾试验箱乃针对各种材质表面处理，包含涂料、电镀、有机及无机及膜，阳极处理，防銹油，化成处理之耐蚀品质，进而达成製品长时间之耐蚀性。

产品规格
规格型号          实验空间（W*D*H）      外箱尺寸（W*D*H）
SH-60             600*450*400mm          1075*630*1100mm
SH-90             900*600*500mm          1415*885*1285mm
SH-120           1200*1000*500mm         1900*1200*1400mm
SH-160           1600*1000*500mm         2300*1200*1400mm
SH-200           2000*1000*500mm         2700*1200*1400mm

可根据客户特别要求，订制非标产品。

三 zui大耗电量：AC 220V 单相3KW 50/60HZ

四 试验温度：
依CNS JIS ASTM GB2423.19规格，可设定式恒温控制
A  盐水喷雾试验：NSS，ACSS
1、试验室：35℃ ± 1℃
2、饱和空气桶：47℃±1℃
B  耐腐蚀试验：CASS（醋酸铜）
1、试验室：50℃ ± 1℃
2、饱和空气桶：63℃ ± 1℃

五 机体结构：
材质：
a、试验室採用P.V.C聚氯乙稀板，耐高温
b、试验室密封盖採用PVC耐冲击板
c、试药补充瓶採用隐藏式附水位表，清洗容易，不易破裂（气压缸自动开闭）
d、饱和空气桶採用SUS#304不锈钢耐高压桶保温效果*
e、试验室盖架採平面分度架，可任意调整角度，四面落雾及受雾方面**，试药片放置数量多

福特标准中规定的相关要求如下：

                        Procedure
A.   Panels
     1.Scribe two diagonal lines from corner to corner across three test panels to the bare metal. Zinc-coated steel panels should be scratched through paint to zinc coating.（Do not penetrate to the bare steel）.
     2.Suspend the panels at an angle in the salt spray cabinet as specified in ASTM B 117 for the fime designated by the material specification （testing side up）.
     3.Rinse the panels with water, blot dry,and examine within 15 minutes.
       Measure and report in mm the maximum corrosion and blister creepage on either side of the scribed lines. Also examine panels for occurrence of surface blisters giving size and density according to ASTM D 714. In case of zinc-coated panels, measure the maximum distance of blisters and raised paint from the scribed line.
     4.Apply tape over each scribed line, in a parallel direction, using firm finger pressure to ensure contact with the panel surface（i.e.,scribe line to be visible）. This step is to be performed within 30 minutes after completion of Step 3.
     5.Within 90 +/- 30 s of application, remove the tape by pulling back rapidly （do not jerk） at as close to an angle of 180°to the panel as possible.

                       Evaluation
Report in mm, corrosion and/or blister creep and loss of adhesion after the tape test from scribed lines and occurrence of blistering and adhesion loss beyond the scribed lines.
B.    Parts
1.Wash parts in water to remove dirt and contamination.
2.Suspend the parts in the salt spray cabinet in car position for the time designated by the individual specification. Parts shall not be scribed unless otherwise requested by the applicable Engineering Specifications, and the position should be varied slightly if recesses tend to collect solution.
3.Rinse the parts with warm water and a soft sponge to remove runoff stain,blot dry and examine within 15 minutes.
4.Apply tape across the surface using firm finger pressure. this step, which is to be performed within 30 minutes after the completion of Step 3, is to help identify blistering.
5.Within 90 +/- 30 s of application, remove the tape by pulling back rapidly （do not jerk） at as close to an angle of 180°to the panel as possible.
 
                        Evaluation
Report occurrence of blistering and corrosion.

Chemicals, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities.